Free API-571 Exam Dumps

Comprehensive and Detailed Explanation From Exact Extract:

According to API RP 571, amine stress corrosion cracking (Amine SCC) is a form of environmentally assisted cracking that occurs in alkanolamine systems (e.g., MEA, DEA, DGA) used for acid gas treating. The cracking mechanism requires the simultaneous presence of tensile stress, susceptible microstructure, and an amine environment.

API RP 571 clearly states that Amine SCC occurs primarily in the weld heat affected zone (HAZ) of carbon and low-alloy steels. The reasons include:

The HAZ contains high residual stresses from welding.

The microstructure in the HAZ is metallurgically altered, making it more susceptible than base metal.

Cracks often initiate adjacent to welds, not in the weld metal itself.

Why the other options are incorrect:

Option A (Weld fusion line) is not the primary cracking location.

Option C (Weld metal) generally has different chemistry and lower susceptibility.

Option D (Base metal) typically has lower residual stress and is less prone.

API RP 571 specifically identifies the weld HAZ as the dominant cracking location for Amine SCC.

Referenced Documents (Study Basis):

API RP 571 -- Section on Amine Stress Corrosion Cracking

API Corrosion and Materials Study Guide